CuYO 2 Thin Films Prepared by Copper Acetate

Copper Acetate Manufacturers(WSDTY) CuYO2 thin films were prepared on SiO2 substrates by the sol-gel method. Prior to deposition of the thin films, the substrates were degreased by ultrasonication in EtOH. Copper (II) acetate monohydrate (Wako Chemicals) was dissolved in a mixture of 2-methoxyethanol and 2-aminoethanol by stirring for 12 h at room temperature. The molar ratio of 2-aminoethanol, chelating agent, to copper acetate was maintained at 4:1 and the color of the solution was dark blue. Yttrium acetate tetrahydrate (Wako Chemicals) was dissolved in a mixture of 2-me- thoxyethanol and 2-aminoethanol by stirring for 12 h at room temperature. The molar ratio of 2-aminoethanol to aluminum acetate basic was maintained at 2:1. After stirring, a colorless homogeneous solution was obtained. The two solutions were mixed with a Cu/Y ratio of 1:1 and stirred at room temperature for 12 h to form a sol.

The sol was with total metal ion concentrations of 0.40 M. The sol was spin-coated onto a SiO2 substrate with spinning speed of 3000 rpm for 5 s. In the case of the samples prepared for transmission spectroscopy measurements, the sol adsorbed on the back side of the substrate was carefully removed after spin-coating. The coated films were first heated at 200?C for 10 min, and then heated again at a higher temperature of 500?C for 20 min using hot-plate-type heating devices. The spin-coating and subsequent heat treatment procedures were repeated for 6 times to obtain the desired film thickness of 0.4 μm. The prepared gel films were finally annealed at temperatures in the range of 750?C – 900?C for 10 h under nitrogen flow. The temperature was increased from room temperature to the specific temperature over a period of 3 h, held at the specific temperature for 10 h, and then cooled to room temperature over 6 h.

Click Copper Acetate to learn about more information

Hinterlasse eine Antwort

Deine E-Mail-Adresse wird nicht veröffentlicht.

Du kannst folgende HTML-Tags benutzen: <a href="" title=""> <abbr title=""> <acronym title=""> <b> <blockquote cite=""> <cite> <code> <del datetime=""> <em> <i> <q cite=""> <strike> <strong>